SECONDARY AND TERTIARY DENDRITIC SPACING ANALYSIS IN 316 L STAINLESS STEEL
In the present work, experimental research was carried out to determine the evolution of dendritic microstructure during the directional solidification of 316-L steel, in which columnar to equiaxed transitions (CET) were also present. Experimental values of secondary (l2) and tertiary (l3) dendritic...